High Temp Wire Insulation Sleeve Copper Insulation Pipe Glass Sleeving

• Color: Black, Yellow, White and Natural
• Feature: Heat Insulation
• Tensile Strength: Good
• Moisture Resistance: Excellent
• Temperature: -55 to 200
• Sample: Free
• Model NO.: Fiberglass Sleeving
• Cut-Through Resistance: Excellent
• Rated Voltage: 35kv or Above
• Radiation Resistance: Excellent
• Type: Insulation Sleeving
• Product Name: Silicone Rubber Coated Sleeving
• Length: 1000mm Per Piece
• OEM,ODM Service: Avaliable
• Application: Dry Transformers and Wire Protection
• Material: Fiberglass Braid
• Transport Package: Rolls, Pallets, Cartons. Wooden Cases
• Trademark: Powerwell
• Origin: Hunan, China
• Production Capacity: 100000 Piece/Pieces Per Month

Product Description

 

 

 

 

Features

Excellent dielectric strength and flexibility

High temperatures up •

Maximum flexibility and expandability

• VW-1

 Chemical resistance

 Moisture resistance

• Cut-through resistance •

 Radiation resistance

• Abrasion resistance

Applications

AC, DC motor lead protection, high current dry transformers and automotive under-the-hood wire protection.

Available

Sizes 

Iin continuous spooled lengths or cut lengths in 1000mm per piece

Colors

Black, yellow, white and natural.

Other colours are available on request

Technical Data

 

Hardness		30 durometer, shore A
Tensile Strength		> 1000 psi
Elongation		> 600%
100% Modulus		300 psi
Tear strength		150 ppi
Compression set		> 8.0% (22 hrs @ 177°C)
Resistance to:
Ozone		excellent
Corona		excellent
Radiation		excellent
Sunlight		excellent
Fungus		excellent
Dielectric Grade		Min. Ave. Breakdown	Min. Indiv.
A		8000V	6000V
B		4000V	2500V
C-1		2500V	1000V
C-2		1500V	800V
	Properties	Requirements		Results obtained
	Prof voltage (kv)	1.5 kv to 12 kv
	Self Extinguish	Flame must extinguish within 45 Secs		Self Extinguishment
	Flexibility (Bending Test)	No crack should be observed when kept at temperature of 180^o C for 72 hours.		No Crack Observed
	Insulation Resistance	10x10^3 M?		OK
	Varnish Stability	No flow of varnish should be noticed when kept at temperature of 180^o C for 72 hours.		No Flow Observed